Use of wood from Pinus caribaea var. caribaea and Pinus caribaea var. bahamensis for production of particleboard panels
Titel:
Use of wood from Pinus caribaea var. caribaea and Pinus caribaea var. bahamensis for production of particleboard panels
Auteur:
Setsuo Iwakiri Alberto Antonio Manhiça Carlos Frederico Alice Parchen Everilton José Cit Rosilani Trianoski
Verschenen in:
Cerne
Paginering:
Jaargang 16 (2010) nr. 2 pagina's 193-198
Jaar:
2010
Inhoud:
This study aimed to evaluate the quality of particleboard panels made with wood from Pinus caribaea var. caribaea andPinus caribaea var. bahamensis, as obtained from forest stands. Experimental panels were produced with a nominal density of 0.70 g/cm³,using urea-formaldehyde resin and wood particles of Pinus caribaea var. caribaea and Pinus caribaea var. bahamensis, at rates of100%x0%, 75%x25%, 50%x50%, 25%x75% and 0%x100%. Pinus taeda wood was used as control sample. Panels were compressed ata specific pressure of 40 kgf/cm² and temperature of 160ºC, for 8 minutes. Analysis results of water absorption, thickness swell, internalbond, modulus of elasticity and modulus of rupture properties indicated feasibility of using wood from Pinus caribaea var. caribaea andPinus caribaea var. bahamensis for production of particleboard panels, individually or combined at rates of 75%, 50% and 25%.