The influence of irradiated wood filler on some properties of polypropylene - wood composites |
| Auteur: |
Điporović-Momčilović Milanka |
| Verschenen in: |
Glasnik Šumarskog Fakulteta |
| Paginering: | Jaargang 2007 (2007) nr. 95 pagina's 73-82 |
| Jaar: |
2007 |
| Inhoud: |
The problem of compatibility between the wood filler and thermoplastic matrix is of essential importance in composite production. Numerous methods have been developed for increasing this compatibility, which is still representing a challenging objective of composite research throughout the world. The research into these methods is primarily directed towards their efficiency from the viewpoint of the composite performance and their economical acceptability. The latter is of particular importance for the composite production in the developing countries with respect to the shortage of the corresponding funds. With this respect, the utilization of ionizing radiation might have considerable advantages. In this research, the beech wood flour was irradiated by a dose of 10 kGy of 60Co gamma rays for purpose of provoking the changes by the ionizing effect. The effects of ionizing radiation upon the properties of wood particles have been examined by IR spectroscopy and by determination of contents of hydroxyl groups in wood by acetylating as an indirect method. All these methods have been expected to reveal the chemical effects of the applied radiation treatment. The irradiated and the control wood flour were used in order to produce the samples of composite with polypropylene. The polypropylene-wood flour (PP-WF) composites were produced with 40% of wood particles having fraction size 0.3 mm. The melt-blended composites were modified with amido-acrylic acid (AMACA) as a new coupling agent synthesized for this propose in amount of 6 wt.% (based on wood filler) and successively with 0.05 wt.% (based on PP) of organic peroxide during mixing step. The composites containing coupling agents showed superior mechanical properties, compared to the untreated one. The highest extent of improvement of tensile was achieved in PP-WFl composites modified with AMACA coupling agent. |
| Uitgever: |
Faculty of Forestry (provided by DOAJ) |
| Bronbestand: |
Elektronische Wetenschappelijke Tijdschriften |
Details van artikel 12 van 13 gevonden artikelen
| << vorige | volgende >> |