| Titel: |
Improved Properties of Polymers Under Hydrostatic Pressure |
| Auteur: |
OI'khovik, E. Figovsky, O. Feigin, V. |
| Verschenen in: |
Materials and manufacturing processes |
| Paginering: | Jaargang 14 (1999) nr. 3 pagina's 427-433 |
| Jaar: |
1999 |
| Inhoud: |
The role of hydrostatic pressure in strengthening of polymer materials was studied. It was established that the orientation crystallization of fibers and films in a high-pressure chamber leads to significant increase of their mechanical properties. The optimal temperature and pressure for the crystallization of polyethylene were determined, providing a static strength of 490 MPa, that is higher than the strength of a type 3 steel. A strength of 100 MPa was achieved for fluorinoplast-4 oriented under pressure at a stretch ratio of about 6. This opens the possibility of obtaining high strength fibers and fabrics using this material. |