| Titel: |
Corrosion Behavior of Vanadium Carbide Coating Produced by a Thermal Diffusion Process |
| Auteur: |
Fazluddin, S. Bhagga Koursaris, A. Ringas, C. Cowie, K. |
| Verschenen in: |
Materials and manufacturing processes |
| Paginering: | Jaargang 10 (1995) nr. 2 pagina's 159-169 |
| Jaar: |
1995-03-01 |
| Inhoud: |
Vanadium carbide coating was deposited on carbon steel (EN9) and mild steel using a thermal diffusion process. Samples were immersed in a molten salt bath containing appropriate carbide forming compounds at temperatures ranging from 850°C to 1100°C. Samples were treated for various lengths of time in order to obtain coatings of various thicknesses. The corrosion behavior of the vanadium carbide coatings was evaluated by accelerated electrochemical tests. The corrosion resistance of the carbide coating was found to be superior to that of the untreated base alloys. |