  Coating Properties of Di- and Tri-functional Epoxy Resin Using Novel Epoxy Based Polyamide as Curing Agent
 
 
Titel: Coating Properties of Di- and Tri-functional Epoxy Resin Using Novel Epoxy Based Polyamide as Curing Agent
Auteur: Baraiya, Rajesh
Patel, Sanjay
Raval, Dipak
Thakkar, Jatin
Verschenen in: International journal of polymeric materials
Paginering: Jaargang 39 (1998) nr. 3-4 pagina's 255-260
Jaar: 1998-02-01
Inhoud: Bis ester namely 1, 1'-(1-methylethylidene) bis[4-{1-(1-imino-4-ethyl benzoate)-2-pro-panolyloxy}]benzene was synthesized by the reaction of epoxy resin, diglycidyl ether of bisphenol-A-(DGEBA) and 4-amino ethyl benzoate (4-AEB) using triethyl amine as catalyst. The synthesized bisester was reacted with two different aliphatic diamines viz., 1. 4-butylene diamine (BDA) and 1. 6-hexamethylene diamine (HMDA) to obtain respective polyamide resins (PAs) abbreviated as DGEBA-4-AEB:BDA and DGEBA-4AEB:HMDA respectively. The PAs synthesized were used as a curing agent for the difunctional epoxy resin, (DGEBA) and trifunctional epoxy resin, (TGPAP) in three different ratios. Using triethylamine as a catalyst and PAs as a curing agent. DGEBA and TGPAP were polymerized on mild steel panels at 120°C for 1 hr. The coated panels thus obtained were tested for scratch hardness, flexibility, impact strength and chemical resistancy. It appears from the results that epoxy resins, DGEBA based polyamides can successfully be used as a curing agent for the coating application.
Uitgever: Taylor & Francis
Bronbestand: Elektronische Wetenschappelijke Tijdschriften
 
 

                             Details van artikel 1 van 12 gevonden artikelen
 
   volgende >>
 
 Koninklijke Bibliotheek - Nationale Bibliotheek van Nederland