  Curing Characteristics and Mechanical Properties of Oil Palm Wood Flour Reinforced Epoxidized Natural Rubber Composites
 
 
Titel: Curing Characteristics and Mechanical Properties of Oil Palm Wood Flour Reinforced Epoxidized Natural Rubber Composites
Auteur: Ismail, Hanafi
Jaffei, R. M.
Verschenen in: International journal of polymeric materials
Paginering: Jaargang 36 (1997) nr. 3-4 pagina's 241-254
Jaar: 1997-04-01
Inhoud: The paper reports on the curing characteristics and mechanical properties of oil palm wood flour (OPWF) reinforced epoxidized natural rubber (ENR) composites. Three sizes of OPWF at different filler loadings were compounded with a two roll mill. The cure (t90) and scorch times of all filler size decrease with increasing OPWF loading. Increasing OPWF loading in ENR compound resulted in reduction of tensile strength and elongation at break but increased tensile modulus, tear strength and hardness. The composites filled with smaller OPWF size showed higher tensile strength, tensile modulus and tear strength. Scanning electron microscope (SEM) micrographs showed that at lower filler loading the fracture of composites occurred mainly due to the breakage of fibre with minimum pull-out of fibres from the matrix. However as the filler loading is increased, the fibre pull-out became very prominent due to the lack of adhesion between fibre and rubber matrix.
Uitgever: Taylor & Francis
Bronbestand: Elektronische Wetenschappelijke Tijdschriften
 
 

                             Details van artikel 1 van 9 gevonden artikelen
 
   volgende >>
 
 Koninklijke Bibliotheek - Nationale Bibliotheek van Nederland