Adhesion of the marine fouling diatom amphora coffeaeformis to non-solid gel surfaces
Titel:
Adhesion of the marine fouling diatom amphora coffeaeformis to non-solid gel surfaces
Auteur:
Rasmussen, Kjetil Østgaard, Kjetill
Verschenen in:
Biofouling
Paginering:
Jaargang 17 (2001) nr. 2 pagina's 103-115
Jaar:
2001-07
Inhoud:
Diatom adhesion to different gel surfaces was tested under different shear conditions, using the fouling marine diatom Amphora coffeaeformis as test organism. Four polymers were selected to obtain a test matrix containing gels with different surface charge as well as different surface energies, viz. agarose, alginate, chitosan and chemically modified polyvinylalcohol (PVA-SbQ). Three experimental systems were applied to obtain different shear rates. Experimental system 1 consisted of gels cast in a cell culturing well plate for comparing initial adhesion as well as long term biofilm development in the absence of shear. In experimental system 2, microscope slide based test surfaces were tested in aquaria under low shear conditions. A rotating annular biofilm reactor was used to obtain high and controlled shear rates. At high shear rates A. coffeaeformis cells adhered better to the charged polymer gels (alginate and chitosan) than to the low charged polymer gels (agarose and PVA-SbQ). In the system where shear was absent A. coffeaeformis cells developed a biofilm on agarose equivalent to the charged polymer gels, while adhesion to PVA-SbQ remained low at all shear rates. It is concluded that non-solid surfaces did not represent an obstacle to settling and growth of this organism. As observed for solid surfaces, low charge density led to reduced attachment, particularly at high shear.
Tijdschrift beschrijving