| Titel: |
Thermal Shock Endurance of Porous Steel with Plasma Sprayed ZrO2 Coating |
| Auteur: |
Kurushima, T. Ishizaki, K. Harada, R. |
| Verschenen in: |
Materials and manufacturing processes |
| Paginering: | Jaargang 9 (1994) nr. 4 pagina's 757-765 |
| Jaar: |
1994-07-01 |
| Inhoud: |
A new thermal shock resistant material has been developed by plasma spraying ZrO3 (stabilized with 7 wt% CaO) on porous steel. When the porosity of the substrate steel is more than 25% and a Ni-Cr undercoating is applied, the ZrO2 coating cracks but does not spall off by water quenching from 1125°C to 25°C. Because the cracks are produced regularly, the water quenching test is considered as a new heat treatment method for high thermal shock endurance of the ZrO2 coatings. This material has gas penetrating capability, and may be used as a permanent casting mold. |