Remaining of ε-iron structure at atmospheric pressure and superlattice formation by shearing at high pressure |
| Auteur: |
Furuihi, H. Fujii, N. Kanno, Y. Ito, E. Watanabe, S. Tanaka, H. |
| Verschenen in: |
High pressure research |
| Paginering: | Jaargang 24 (2004) nr. 3 pagina's 385-389 |
| Jaar: |
2004-09 |
| Inhoud: |
Transmission X-ray diffraction pattern of iron sheared at high pressure show rings whose interplanar spacings correspond to those of ε-iron and their integral multiple, in spite of the fact that it has been kept at atmospheric pressure for ∼3 months from the shearing. This and other related phenomena suggest that the pattern corresponds to the remains of the ε-iron structure in which superlattice formed. The volume of the specimen at atmospheric pressure after elapsing ∼3 months at atmospheric pressure from the shearing was 86% of that before the shearing. |