| Titel: |
A low frequency Raman study of SrBi2Ta2O9-Bi3TiNbO9 |
| Auteur: |
Ching-Prado, E. Perez, W. Reynes-Figueroa, A. Katiyar, R. S. Desu, S. B. |
| Verschenen in: |
Ferroelectrics letters section |
| Paginering: | Jaargang 25 (1999) nr. 1-2 pagina's 53-57 |
| Jaar: |
1999-04-01 |
| Inhoud: |
Raman spectra of SrBi2Ta2O9 (SBT), Bi3TiNbO9(BTN), and x(SBT) + (1-x)(BTN) samples were studied for the first time in the low frequency region. The BTN spectra show two features around 33 and 41 cm-1, while only one feature, around 30 cm-1, is found in SBT. The stoichiometric evolution of the Raman spectra shows that the frequency positions of these bands decrease as x changes from 0 to 1. Strong correlation is found between the frequency positions of these modes and both the Curie temperature and the a-parameter. The results are interpreted in terms of the ferroelectric displacive modes, which are responsible for the strong spontaneous polarization along a-axis. The band around 65 cm-1is assigned to oxygen motion in the B2O2 layer. |